Effect of W additions on the structural and magnetic properties of Ni<inf>50</inf>Ti<inf>50</inf><inf>-</inf><inf>x</inf>W<inf>x</inf> and Ti<inf>50</inf>Ni<inf>50</inf><inf>-</inf><inf>x</inf>W<inf>x</inf> systems obtained by mechanical alloying

Abstract:

The effect of tungsten (Wx) additions (x = 0.5, 1.0, 1.5 and 2.0 at.%), on the structural and magnetic properties of the binary systems Ni50Ti50-x and Ti50Ni50-x obtained by mechanical alloying was studied. The elementary powders were milled in a Spex 8000 horizontal mill, under N2 atmosphere, for 5 and 20 h. After 20 h of milling a homogenous microstructure was observed, particularly for small W additions. For this milling time a mixed of nanocrystalline and amorphous structure was obtained. As W concentration increases (1, 1.5 and 2 at.%), in both systems, the presence of small β-W reflections and the presence of very small peaks corresponding to the formation of an incipient new phase, identified as a NiTi(W) solid solution was observed, especially evident for 2 at.%W. The saturation magnetization and magnetic remanence decreases with the addition of W down to a minimum value at 1.5 at.%W, for both systems. The samples were characterized by SEM, EDS, XRD and magnetic measurements by VSM. The structural and magnetic behavior for both ternary alloys was very similar with the W additions.