Effect of the dispersing agent on the structural and magnetic properties of CoFe<inf>2</inf>O<inf>4</inf>/SiO<inf>2</inf> nanocomposites

Abstract:

Cobalt ferrite nanoparticles CoFe2O4 were synthesized using the thermal decomposition method; subsequently the NPs were functionalized using poli vinyl pyrrolidone (PVP) cetyl trimethyl ammonium bromide (CTAB) and polyethylene glycol (PEG) as dispersing agent. Surface modification with silica SiO2 was made using the Stöber method and tetraethyl orthosilicate (TEOS) as precursor. The purpose of this study is to investigate the influence of the different dispersing agents on the structure and therefore on the magnetic properties of the CoFe2O4/SiO2 nanocomposites. Structural characterization was carried out using: X-ray diffraction (XRD), infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Magnetic properties were evaluated using a vibrating sample magnetometer (VSM) at room temperature. Our results revealed that the structural and magnetic properties of the CoFe2O4/SiO2 nanocomposites were significantly different depending of the type of dispersing agents used before the surface modification with silica SiO2.