Electrochemical properties of TiWN/TiWC multilayer coatings deposited by RF-magnetron sputtering on AISI 1060

Abstract:

Nitride and carbide ternary coatings improve the wear and corrosion resistance of carbon steel substrates. In this work, Ti-W-N and Ti-W-C coatings were deposited on AISI 1060 steel sub-strates using reactive radio frequency (RF) magnetron sputtering. The coatings were designed as monolayers, bilayers, and multilayers of 40 periods. The coatings were obtained with simultaneous sputtering of Ti and W targets. The microstructure, composition, and electrochemical properties were investigated by techniques such as X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), atomic force microscopy (AFM), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization. XRD results shower a mix of binary TiN and W2 N structures in the Ti-W-N layer, a ternary phase in Ti-W-C layers, in addition of a quater-nary phase of Ti-W-CN in the multilayers. The analysis of the XPS demonstrated that the atomic concentration of Ti was more significant than W in the Ti-W-N and Ti-W-C layers. The lowest corrosion rate (0.19 mm/year−1) and highest impedance (~10 kΩ·cm2) out of all coatings were found in n = 40 bilayers. In the simulation of equivalent electrical circuits, it was found that the Ti-W-N coating presented three processes of impedance (Pore resistance + Coating + Inductance). However, the multilayer (n = 40) system presented a major dielectric constant through the electrolyte adsorption; therefore, this caused an increase in the capacitance of the coating.