Effect of molecular weight reduction by gamma irradiation on chitosan film properties

Abstract:

The present work aimed the influence of molecular weight (MW) reduction by irradiation with ⁶⁰Co and polymer concentration on some physical properties of chitosan films. Irradiation of chitosan with a MW of 275.221 kDa and 74.74% of deacetylation degree was performed using a ⁶⁰Co source to provide doses of 5, 10, 20 and 50 kGy to obtain chitosans with molecular weights of 247.847, 221.563, 126.469 and 77.063 kDa, respectively. Films were prepared via the solution casting method. Film-forming solutions (FFS) of chitosan irradiated or not, were prepared at 1.5 and 2% (w/v) in a solution of lactic acid at 1% (v/v) and 0.1% (v/v) of Tween 80. The FFS were poured into glass plates of 400 cm² and dried at 60 °C during 10 h without airflow. The decrease of MW and increase of chitosan concentration increased the tensil strength and water vapor permeability while decreased the elongation at break of the films. The chitosan MW did not significantly influence (p > 0.05) the water solubility of films within a same polymer concentration. There was a decrease in the films' brightness with the increase of concentration and a decrease of the MW of irradiated chitosan, while the b∗values of films increased and there was an increasing tendency of their apparent opacity.

Año de publicación:

2015

Keywords:

• Mechanical properties
• films
• Chitosan
• Water vapor permeability
• Gamma irradiation

Fuente:

scopus

google